PROPERTIES AND SINTERING BEHAVIOUR OF FINE SPHERICAL IRON ...

PROPERTIES AND SINTERING BEHAVIOUR OF FINE SPHERICAL IRON ...

Under argon metal powder with an average particle diameter d 50 between 10 and 80 µm can be manufactured [1, 2, 3]. Usual fine particle fraction will be sieved. The manufacturing of iron powders < 10 µm is based on the iron carbonyl process [4]. Both technologies are expensive processes and the powder cost are in the range of 7-10 €/kg, This powders are used as binder matrix in diamond ...

Continue Reading...
Analysis of Dewaxing Behavior of Iron Powder Compacts ...

Analysis of Dewaxing Behavior of Iron Powder Compacts ...

and green compact in the case described above, under conditions simulating commercial operation, is consid-ered useful for understanding the phenomena involved. For example, Kondoh et al. developed a uniform filling technique by a direct understanding and visualization of the flow behavior of iron powder into the die cavity7). At JFE Steel, dewaxing behavior of iron powder com-pacts placed in ...

Continue Reading...
Manufacturing of Fine Spherical Iron Powder and the ...

Manufacturing of Fine Spherical Iron Powder and the ...

Under argon metal powder with an average particle diameter d 50 between 10 and 80 µm can be manufactured [4, 5, 6]. Usual fine particle fraction will be sieved. The manufacturing of iron powders ...

Continue Reading...
Manufacturing of Fine Spherical Iron Powder and the ...

Manufacturing of Fine Spherical Iron Powder and the ...

CO full reduction of iron oxide only by high temperatures (>1000 °C) formation of a strong sinter cake temperature dependence of the reduction of iron oxide under H 2 and CO [M. Wiberg] [%] reduction temperature [%] H2-reduction 1st temperature step full reduction between 500°C and 600 °C pyrophoric powder (specific surface >> 1 m²/g)

Continue Reading...
DI: 10.1590/S1516-14392011005000074 Strain Hardening ...

DI: 10.1590/S1516-14392011005000074 Strain Hardening ...

behavior of an aluminum-iron powder metallurgy composite with various percent of iron contents and for the various stress state conditions with two different aspect ratios. It is well known that both the strain hardening exponent and the strength coefficient are basic mechanical behaviour performance parameters of metallic materials. Therefore, the strain-hardening exponent is an important ...

Continue Reading...
Prediction model for surface temperature of roller and ...

Prediction model for surface temperature of roller and ...

surface temperature of roller were measured under several rotating speeds of roller. These experimental results could be quantitatively described by using a mathematical model including the torque effect of roller, which was derived based on the steady-state heat transfer during hot roll pressing. In addition, the densification behavior of iron powder during the hot roll pressing was ...

Continue Reading...
Balling behavior of stainless steel and nickel powder ...

Balling behavior of stainless steel and nickel powder ...

under high scan speed. Kruth et al. analyzed the addition of deoxidizer into powder system to alleviate the balling level [8]. Simchi and Pohl researched the surface conditions of pure iron powder under different scan line spacings, pointing out that the balling was because of capillary instability and the balling can be lessened by reducing the

Continue Reading...
Ultra high frequency induction welding of powder metal ...

Ultra high frequency induction welding of powder metal ...

In iron powder metallurgy, common sintering conditions are: 15–60 minutes at 1120–1150 °C (German, 1996). Particles of com-mercial iron powders for structural parts are usually ≤150 μm. Iron-copper-carbon alloys illustrate the unique properties possible by PM (German, 1996). Copper and graphite (carbon) are mixed with iron

Continue Reading...
WORKABILITY BEHAVIOR OF POWDER METALLURGY CARBIDE ...

WORKABILITY BEHAVIOR OF POWDER METALLURGY CARBIDE ...

WORKABILITY BEHAVIOR OF POWDER METALLURGY CARBIDE REINFORCED ALUMINUM COMPOSITES DURING HOT FORGING ... (Mo 2C), iron carbide (Fe 3C) and tungsten carbide (WC) reinforcements on the composite aluminium compacts. The hot deformation of the carbide reinforce aluminium compacts, Al-2TiC, Al-2WC, Al-2Fe 3C and Al-2Mo 2C, with aspect ratios (AR) of 0.4 and 0.6, was carried out and the workability ...

Continue Reading...
Reinforcing Behaviors of Sulfur-Containing Silane Coupling ...

Reinforcing Behaviors of Sulfur-Containing Silane Coupling ...

mechanical behavior; sulfur contribution e ect 1. Introduction Magnetorheological elastomers (MREs) are largely composed of a rubber matrix and soft magnetic particles [1,2]. MREs belong to a new type of intelligent material since the rheological properties can be transformed reversibly and rapidly by applying external magnetic fields [3–5]. Typically, components of MREs are cured under a ...

Continue Reading...
Oxidation of Stainless Steel Powder

Oxidation of Stainless Steel Powder

Abstract To understand the corrosion behavior of a model 304L(p)– ZrO 2(s) composite, a 304L stainless steel powder was studied under oxygen at high temperature. Oxidation tests were performed with thermogravimetry. The so-called jumps method, which involves a sudden change of the temperature, was also applied to propose a kinetic model. Two ...

Continue Reading...